Examination of Structral Morphological and Magnetic Behaviour of Znfe2o4 Nanoparticle Synthesised by Co-Pricipitation Method
C. Sambath Kumar1, S. Ezhil Arasi2, B. Natarajan3, A. Arivarasan4, P. Devendran5
1P. Devendran, Department of Physics, International Research Centre, Kalasalingam Academy of Research and Education, Krishnankoil (Tamil Nadu), India.
2C. Sambath Kumar, Department of Chemistry, SRM Institute of Science and Technology, Kattankulathur, Chennai (Tamil Nadu), India.
3S. Ezhil Arasi, Department of Chemistry, SRM Institute of Science and Technology, Kattankulathur, Chennai (Tamil Nadu), India.
4B. Natarajan, Department of Chemistry, SRM Institute of Science and Technology, Kattankulathur, Chennai (Tamil Nadu), India.
5A. Arivarasan, Department of Chemistry, SRM Institute of Science and Technology, Kattankulathur, Chennai (Tamil Nadu), India.
Manuscript received on 25 November 2019 | Revised Manuscript received on 19 December 2019 | Manuscript Published on 30 December 2019 | PP: 1085-1088 | Volume-9 Issue-1S4 December 2019 | Retrieval Number: A11901291S419/19©BEIESP | DOI: 10.35940/ijeat.A1190.1291S419
Open Access | Editorial and Publishing Policies | Cite | Mendeley | Indexing and Abstracting
© The Authors. Blue Eyes Intelligence Engineering and Sciences Publication (BEIESP). This is an open access article under the CC-BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/)

Abstract: The Zinc Ferrites (ZnFe2O4 ) nanoparticles (NPs) successfully synthesized by co-precipitation method. As prepared NPs were annealed withdifferent temperature at 800 and 1000C. The crystalline phase, surface morphology andelemental distribution were confirmed by XRD, SEM and EDS respectively. The prepared ZnFe2O4XRD pattern confirm the cubic crystalline nature. The surface morphology of the prepared sample was found irregular rock like structure due to ferric metal. FTIR, EDS studies prove charactristics behavioural vibration of Zn-Fe-O elements and purity of the sample correspondingly. Prepared ZnFe2O4 sample exhibit a super paramagnetic nature with the saturated magnetization of 22.066 emu/g and coercivity of 15 Oe by VSM analysis.
Keywords: Zinc-Ferrite Nps, Co-Precipitation, High-Density Magnetic Storage Media, Super Paramagnetic.